Take advantage of our exclusive offers:
- - Oferta 4 Luxacore Z + LuxaBond Universal
- - Oferta varfuri Automix bleu
- - Oferta Etch-37
- - Oferta TheraCal LC 4 buc cu discount
- - Oferta MultiCal
- - Oferta 100 periute detartraj cu discount
- - Oferta 12 oglinzi plane nr4 Asa cu discount
- - Oferta CaviWipes 4 cutii cu discount
- - Oferta 2 anse XPEDENT cu 15% discount
- - Oferta 3 anse XPEDENT cu 20% discount
- - Oferta Varfuri Automix albastru/rosu
- - Oferta varfuri Automix verzi
- - Oferta pietre Arkansas (turbina)
- - Pachete UF >3 cu 10% disc
- - 5 Discuri Yucera cu 25% disc
- - Oferta Varfuri Automix galbene
- - Apatos Mix granulatie mare - Oferta 3+1
- - Oferta Ecosite 2+1
Katana HT 14mm zirconium disc
Zirconium disc, High Translucency, for frameworks, bridges, crowns
Noritake Katana HT (High Translucency) is a highly durable, high translucency monochrome zirconium suitable for milling ceramic veneering frameworks (crowns and bridges, anterior and posterior, of any size).
KATANA multi-layer zirconium discs, known for fast Full-Contour/Monolithic restorations, are now sinterable in 90 minutes (in fast sintering furnaces*) *Tested for AUSTROMAT 674i, inFire HTC speed and Sintra Plus furnaces; valid for Katana ML/HT, STML/UTML zirconia discs.
Translucency for 1 mm thickness:
Flexural strength
Extraordinary durability due to reduced monoclinic transformation Under hydrothermal conditions, the tetragonal system of the zirconium surface becomes monoclinic and brittle. KATANA zirconia, however, has a minimal monoclinic transformation rate, maintaining its hardness over time.
Technical details:
diameter - 98.5mm
thickness - 14mm
flexural strength - 1050-1100 MPa
fracture strength - 5Mpa√m
Available shades: HT10: white, HT12:A1, B1, B2 and HT13: A2, A3
Katana HT is recommended to be ceramic coated to obtain the desired shade
Further information can be found in the User's Guide: Ghidul de utilizare